Microelectronic device with anti-stiction coating

ABSTRACT

One embodiment of a microelectronic device includes a movable plate including a lower surface, a bump positioned on the lower surface, and an anti-stiction coating positioned only on the bump.

BACKGROUND

Microelectronic devices, such as microelectromechanical devices (MEMS),may include a movable member, such as a movable reflective plate,positioned on a substrate. The movable member may be positioned justabove a surface of the substrate such that a spacing between the movablemember and the substrate may be only a few hundred nanometers and may bevaried by movement of the movable member. A bump may be positionedbetween the movable member and the substrate to maintain the spacingduring movement of the movable member. Stiction forces may build up onthe movable member and/or the bump which may hinder movement of themovable member. The stiction forces may arise from dielectric chargetrapping, capillary forces, and/or van de Waals forces. It may bedesirable to coat the bump so as to reduce the stiction forces on thebump and/or the movable member.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic top view of one embodiment of a wafer including aplurality of microelectronic devices thereon.

FIG. 2 is a schematic top view of one embodiment of a microelectronicdevice.

FIGS. 3 and 4 are schematic cross-sectional side views of one embodimentof a microelectronic device, including one embodiment of ananti-stiction device and coating thereon, in an unbiased and a biasedcondition, respectively.

FIG. 5 is a schematic cross-sectional side view of one embodiment of aprocess of applying one embodiment of an anti-stiction coating.

DETAILED DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic top view of one embodiment of a wafer 10 includinga plurality of microelectronic devices 12 thereon. Wafer 10 may bemanufactured such that each of microelectronic devices 12 includes oneor more bumps or bump regions 14 (see FIG. 3) so as to space each device12 from a substrate 16. In the exemplary embodiment, devices 12 may eachcomprise a microelectromechanical device (MEMS) including a movablemember, such as a movable reflective plate 18 (see FIG. 2). Movablereflective plate 18 (see FIG. 2) and substrate 16 together may comprisean interferometer, such as an optical Fabry-Perot interferometer. Eachof devices 12 may be manufactured simultaneously on wafer 10 so as toreduce manufacturing costs of the devices.

FIG. 2 is a schematic top view of one embodiment of a microelectronicdevice 12. Device 12 may include movable reflective plate 18 movablymounted on substrate 16 by a plurality of posts 20 and a plurality offlexure members 22 captured by posts 20. Reflective plate 18 may includea top surface 19 that is reflective, a lower surface 28 that isreflective, or top and bottom reflective surfaces. Posts 20 and flexuremembers 22 may provide a nominal spacing 24 (see FIG. 3) between movablereflective plate 18 and substrate 16 in the absence of an outside forceon movable plate 18 and substrate 16. In operation a voltage may beapplied between reflective plate 18 and substrate 16 which may causemovable reflective plate 18 to move with respect to substrate 16.Movement of plate 18 may change a height 26 (see FIG. 3) of spacing 24,wherein the voltage force on movable plate 18 may overcome the staticforce of flexures 22. When the voltage is removed from movable plate 18and substrate 16, flexure members 22 may restore movable plate 18 backinto the nominal position above substrate 16. Flexure members 22 may besubstantially evenly spaced around a perimeter of plate 18 such thatflexure members 22 may operate to move plate 18 toward and away fromsubstrate 16 while maintaining the plate substantially parallel to thesubstrate. Flexure member 22 may be manufactured of any flexiblematerial, and in the embodiment shown may be manufactured of tantalumaluminum (TaAl), and posts 20 may be manufactured of TaAl with siliconor silicon nitride dispersed therein Flexure members 22 and posts 20 maybe manufactured by deposition and etching processes.

Bumps 14 (shown in dash lines) may be positioned between reflectiveplate 18 and substrate 16. In the exemplary embodiment, bumps 14 may bepositioned on an underside 28 (see FIG. 3) of plate 18. In particular,in the exemplary embodiment, movable plate 18 may include five bumps 14,one in each corner 18 a of the movable plate and one positioned in acentral region 18 b of plate 18. In other embodiments bumps 14 may bepositioned on substrate 16 or otherwise positioned between the plate andthe substrate such as defining a separate structure. In the embodimentshown, during application of a voltage between plate 18 and substrate16, the plate and the substrate may not contact one another, but bumps14 may contact substrate 16. In other words, bumps 14 may define aminimum height 26 of spacing 24 (see FIG. 3). Bumps 14 may bemanufactured of a nonconductive material, such as a dielectric, suchthat contact of bumps 14 with substrate 16 may not result in electricalconductivity between plate 18 and substrate 16.

During contact of bumps 14 with substrate 16 a stiction force may arisebetween bumps 14 and substrate 16. A stiction force may be defined asthe force utilized to cause one body in contact with another body toremain in contact such that the stiction force may be overcome to moveone body relative to another. Examples of stiction forces may includedielectric charge trapping, capillary forces, and van der Waals forces.Capillary forces may arise during conditions of high humidity, such as arelative humidity of thirty percent or more. Charge trapping and van derWaals forces may arise at very short distances, such as within the closespacing of movable plate 18 and substrate 16 of a MEMS device. Thesestiction forces may tend to retain bumps 14 in contact with substrate 16after the voltage is removed from the plate and the substrate. Thiscontinued contact between plate 18 and substrate 16 after removal of thevoltage may result in a continued small spacing 24 between plate 18 andsubstrate 16, which may result in undesirable reflection of light frommovable reflective plate 18. In other words, the stiction forces onbumps 14 may result in malfunction of reflective plate 18 in theunbiased condition. Accordingly, it may be desirable to coat bumps 14with an anti-stiction coating 30 (see FIG. 3) to decrease and overcomethe stiction force.

FIG. 3 is a schematic cross-sectional side view of one embodiment ofmicroelectronic device 12, including one embodiment of bump 14 withcoating 30 thereon. FIG. 3 shows plate 18 in an unbiased condition,i.e., in a condition where no voltage is applied to plate 18 andsubstrate 16. In this condition, flexure members 22 (see FIG. 2) mayretain spacing 24 between plate 18 and substrate 16 at a height 26 ofless than approximately 800 nanometers, wherein height 26 may be in arange of 400 to 600 nanometers, for example. In the embodiment whereinsubstrate 16 may include a reflective surface 16 a, this nominal orunbiased height 26 of spacing 24 may position plate 18 with respect tosubstrate 16 such that spacing 24 defines a first interference distance26 a that may result in an incoming light 31 being transmitted orfiltered as a first light 32 from device 12. First light 32 may be aparticular color of light such as green, red or blue, or may be a fullspectrum of light, such as white light.

FIG. 4 shows plate 18 in a biased condition, i.e., in a condition wherea voltage is applied to plate 18 and substrate 16. In this condition, aforce of flexure members 22 (see FIG. 2) may be overcome by the appliedvoltage such that plate 18 and substrate 16 may be spaced by a height 26of less than approximately 50 nanometers. In the embodiment whereinsubstrate 16 may include a reflective surface 16 a, this biased height26 of spacing 24 may position plate 18 with respect to substrate 16 suchthat spacing 24 defines a second interference distance 26 b that mayresult in an incoming light 33 being transmitted for filtered as asecond light 34 from device 12. Second light 34 may be an image or acolored light having a high resolution due to the interference fringescreated by the position of plate 18 with respect to substrate 16. Secondlight 34 may be a particular color of light, wherein the color may bedefined by the height 26 b of spacing 24. As height 26 b is varied,light 34 may be varied. In a completely lowered position of plate 18,wherein height 26 b is approximately the same as height 14 c of bump 14and coating 30, such as approximately 50 nanometers, light 34 may besubstantially an absence of light, i.e., a black state. Accordingly, ina completely lowered position, plate 18 may be in an “off” condition.The plate 18 may be referred to as being in the “on” position in allpositions but the fully lowered position. In one embodiment, whereinheight 14 c of bump 14 and coating 30 is 50 nanometers, and height 26 ais 450 nanometers, the travel distance of plate 18 is approximately 400nanometers, which may provide green light from plate 18.

Still referring to FIG. 4, bump 14 is shown in contact with or veryclose to substrate 16. Bump 14 may have a height 14 a of at mostapproximately 50 nanometers, and approximately less than 40 nanometers,and a width 14 b of approximately 200 nanometers. Bump 14 is shownhaving anti-stiction coating 30 thereon, wherein coating 30 may have aheight 30 a (shown larger than scale for ease of illustration) ofapproximately 1.5 nanometers (15 Angstroms), and may be in a range ofapproximately 10 to 15 Angstroms or less. Accordingly, bump 14 withcoating 30 thereon may have a height 14 c of at most approximately 60nanometers. Anti-stiction coating 30 acts to reduce the effect ofstiction forces on bump 14 such that when a voltage is removed fromplate 18 and substrate 16, bump 14 easily moves away from substrate 16by the force of flexure members 22 (see FIG. 2). Coating 30 may bepositioned only in bump region 14 but not in a remainder of underside 28of movable plate 18, as will be described below.

Referring to FIGS. 3 and 4, in the embodiment shown, plate 18 includes afirst region 40, including bump 14, manufactured of an oxide materialsuch as a dielectric insulator, namely, silicon oxide. Bumps 14 may bemanufactured on underside 28 of plate 18 by a process of etching, or anyother process as may be desired. Plate 18 also includes a second region42, that may define lower surface 28, manufactured of a conductivematerial, such as tantalum aluminum (TaAl). In another embodiment,second region 42 may be manufactured of aluminum copper (AlCu). Secondregion 42 may extend over substantially the entire surface of lowersurface 28, except for bump regions 14. Similarly, substrate 16 mayinclude a region 44 in an upper region of the substrate that may bemanufactured of a conductive material, such as TaAl or AlCu. A voltagemay be applied to plate 18 and substrate 16 by application of a voltageto second region 42 of plate 18 and to region 44 of substrate 16. Forexample, in one embodiment, a voltage of approximately 6 volts isapplied across plate 18 and substrate 16 to induce a desired spacing 26b therebetween, wherein spacing 26 b may provide a desiredinterferometer spacing of plate 18 and substrate 16 so as to provide adesired color of light from movable plate 18.

FIG. 5 is a schematic cross-sectional side view of one embodiment of aprocess of applying one embodiment of anti-stiction coating 30 to bumpregions 14. In this embodiment, coating 30 (see FIG. 3) is applied byvapor deposition in an enclosed deposition chamber 46 with the use of avacuum pump 48 to reduce the total pressure within chamber 46. In oneembodiment, vapor deposition is initiated when the pressure withinchamber 46 is approximately 100 millitorr. A total partial pressure ofapproximately 100 to 900 millitorr of a precursor material, such assilane 50, may be introduced to chamber 46 and wafer 10 positionedtherein. Immediately after addition of the silane 50, a catalyst, suchas an approximately equal amount of either water vapor or acetic acidvapor 52 may be introduced to chamber 46. The silane 50, as catalyzed bythe water or acetic acid 52, reacts selectively with the dielectricmaterial of bump regions 14 on wafer 10, i.e., the precursor 50 isnon-reactive with the conductive or metallic material of second region42 of plate 18. In particular, the Si—Cl or the Si(OCH3) bond is broken,with the subsequent reaction of water condensation to form a Si—O—Si(surface) bond. The reaction is allowed to go to completion at atemperature of approximately 35 to 45 degrees Celsius for approximatelytwenty minutes, and more particularly, approximately less than fifteenminutes. Deposition chamber 46 may then be evacuated to remove anyresidual hydrochloric acid, alcohol or water and any unreacted reactantsfrom the chamber. Chamber 46 may then be flushed with an inert gas, suchas nitrogen 54, and opened to the atmosphere. Wafer 10 within chamber 46may then be heated at approximately less than one hundred and twentydegrees Celsius, and more particularly, at approximately one hundred andten degrees Celsius, for greater than forty minutes and less than onehundred minutes, and more particularly, for approximately one hour, toalign the molecules properly on the surface of bump regions 14 to formself-assembled monolayers of coating 30. “Self-assembled monolayers” maybe described, in one example, as the molecules arranging themselves suchthat the fluorinated tail end of the carbon chains align themselves asfar away from the substrate surface as possible such that the carbonchains are positioned substantially perpendicular to the surface of thesubstrate. Alternatively, alignment may be allowed to occur at ambienttemperature over several days.

Coating 30 may comprise a hydrocarbon, such as a fluorinated long-chainsilane which may readily react with the dielectric bump regions 14 ofplate 18, but not with the metallic conductive regions 42 of plate 18.Accordingly, coating 30 may be manufactured of a material thatselectively coats bump regions 14 while not coating a remainder of plate18. In general, coating 30 may be reacted from a precursor 50, such as afluorinated silane, and a catalyst 52. In particular, precursor 50 maybe fluorinated octyltrichlorosilane (FOTS), fluorinateddecyltrichlorosilane (FDTS), dichlorodimethylsilane (DDMS),octyltrichlorosilane (OTS) octadecyltrichlorosilane (ODTS),perfluorobenzoic acid and perfluorooctanoic acid. Catalyst 52 may bewater or acetic acid. The coating material generated may be hydrophobicand may provide protection against humidity controlled attractivecapillary forces that may tend to adhere bump regions 14 to substrate16. Coating 30 may act as a lubricant that may prevent humidity fromaccumulating on bump 14 by forming a conformal coating, such as withDDMS, or by forming self-assembled monolayers (SAMS), such as with FOTS,FDTS, OTS and ODTS. When the silane utilized is fluorinated, there mayalso be repulsive forces between coating 30 and a water condensate inspacing 24 because the fluorines may repel each other. Each of FOTS,FDTS, DDMS, OTS and ODTS may be reacted in chamber 46 as the alkoxy,wherein each chloride may be substituted by a —OCH3 or —OCH2CH3 group.However, the alkoxysilanes may not be as reactive as other compounds andmay utilize longer reaction times or higher temperatures for thereaction to be completed. Additionally, the alkoxysilanes may utilizeboth water and acetic acid simultaneously as a catalyst. Afterdeposition of coating 30, the individual devices 12 may be separated, bycutting wafer 10, and then individually packaged.

The vapor deposition process may further include one or morepretreatment steps. In a first pretreatment step, the density of thereacted silane of coating 30 may be augmented by use of a pretreatmentmaterial 56, such as a water plasma or an oxygen plasma pretreatmentmaterial. During this cleaning and activation pretreatment step, bumpregions 14 of wafer 10 may be exposed to the water plasma or oxygenplasma 56 for a time period of approximately five minutes at an ambienttemperature and a flow rate of approximately 100 standard cubiccentimeters per minute (sccm) at a power of approximately 200 Watts.Both pretreatment materials listed may generate more silanol (SiOH)groups on the surface of bump regions 14 which may then be reacted withthe trichlorosilanes listed above. The greater surface density of thereacted silanes on the surface of coating 30 may render the coating morehydrophobic and thus more protected against stiction forces.

The vapor deposition process described above is relatively quick,reproducible and economical. The amount of material deposited as coating30 may be relatively small because only a monolayer may be utilized andbecause the coating is selectively deposited only on bump regions 14 ofplate 18. When FOTS is utilized as the coating material, a monolayer ofless than twenty Angstroms thick, and more particularly, about 12Angstroms thick, may be sufficient to provide anti-stiction propertiesto bump regions 14. Providing a relatively thin coating 30 may bedesired because full travel of plate 18 with respect to substrate 16 maypermit full functioning of the movable plate, i.e., the ability of theplate of reach a substantially full black state by movement of the platetoward substrate 16.

In another embodiment, coating 30 may be applied as a liquid solutionwherein wafer 10 is coated with the solution. The wafer is then removedfrom the liquid solution and dried. This method of application mayresult in capillary forces between movable plate 18 and substrate 16 dueto the use of a liquid solution. The thickness of coating 30 may bedifficult to control when the coating is applied in condensed phases andthe amount of material supplied may be difficult to accurately measure.In addition, during liquid solution deposition, undesirable particlesmay be deposited. Accordingly, the vapor deposition method discussedabove may be more reliable, more cost effective and more efficient. Instill another embodiment, the anti-stiction coating material may beplaced within the MEMs packaging. The anti-stiction coating material maythen be activated to coat only the bump regions 14 after the MEMs device12 is sealed within its individual package.

In other embodiments a deposition process may be utilized wherein asingle device 12 is individually coated wherein coating 30 selectivelycoats only bump regions 14 and not a remainder of device 12. However,simultaneously coating each. of bump regions 14 on an entire wafer 10may be more efficient.

Another pretreatment step may also be conducted. In this pretreatmentstep MEMs device 12 may be treated with a carboxylic acid 58, such asbenzoic acid, perfluorobenzoic acid, lauric acid, or perfluorooctanoicacid, in vapor form. The pretreatment may be conducted under vacuum indeposition chamber 46 at a temperature in a range of 35 to 45 degreesCelsius, with a pressure of carboxylic acid 58 of approximately 200 to700 millitorr for a time period of approximately ten to fifteen minutes.Carboxylic acid 58 may attach itself to aluminum and/or aluminum oxideson the TaAl surfaces of wafer 10, such as second region 42 of plate 18and region 44 of substrate 16 of devices 12. The carboxylic acid 58 maynot react with the oxide of bump regions 14, such as the TEOS material.This carboxylic acid pretreatment step is thought to chelate thealuminum sites on the surface of the TaAl layer which may reduce oreliminate the anti-stiction coating from being deposited on the non-bumpregions 14 of device 12. Accordingly, this pretreatment step facilitatesdeposition of anti-stiction coating 30 on only bump regions 14 of device12. This carboxylic acid pretreatment step may also increase shunting ofelectrical charge on the surface of the deposited carboxylic acid to theconductive surfaces, such as second region 42 of plate 18 and region 44of substrate 16, thereby reducing charge trapping stiction forces ondevice 12. After the carboxylic acid pretreatment step, wafer 10 mayundergo deposition of anti-stiction coating 30, as described above,which may be selectively deposited only on bump regions 14.

Other variations and modifications of the concepts described herein maybe utilized and fall within the scope of the claims below.

1. A microelectronic device, comprising: a movable plate including alower surface; a bump positioned on said lower surface; and ananti-stiction coating positioned only on said bump.
 2. The device ofclaim 1 wherein said microelectronic device comprises a microelectricalmechanical device.
 3. The device of claim 1 wherein said anti-stictioncoating is deposited on said bump by vapor deposition.
 4. The device ofclaim 1 wherein said anti-stiction coating is a fluorinated long-chainsilane.
 5. The device of claim 1 wherein said bump is manufactured of adielectric material.
 6. The device of claim 1 wherein said bump ismanufactured of silicon dioxide.
 7. The device of claim 1 wherein saidanti-stiction coating is manufactured of a precursor chosen from one offluorinated octyltrichlorosilane (FOTS), fluorinateddecyltrichlorosilane (FDTS), dichlorodimethylsilane (DDMS),octyltrichlorosilane (OTS) and octadecyltrichlorosilane (ODTS).
 8. Thedevice of claim 1 wherein said anti-stiction coating is hydrophobic. 9.The device of claim 1 wherein said device comprises a Fabry-Perotinterferometer.
 10. The device of claim 1 further comprising asubstrate, wherein said plate is movably mounted on said substrate andsaid bump moves into and out of contact with said substrate duringmovement of said plate.
 11. The device of claim 1 wherein said bumpextends outwardly from said lower surface a distance of at most 60nanometers.
 12. A process of manufacturing a microelectronic device,comprising: placing a wafer in a deposition chamber, said waferincluding a plurality of anti-stiction bump regions; and depositing ananti-stiction coating only on said bump regions.
 13. The process ofclaim 12 wherein said wafer includes a plurality of microelectronicdevices and wherein said process further comprises separating and thenindividually packaging said microelectronic devices.
 14. The process ofclaim 12 wherein each of said microelectronic devices includes aplurality of bump regions.
 15. The process of claim 12 wherein saiddepositing comprises vapor depositing a fluorinated long-chain silaneonly on said bump regions.
 16. The process of claim 12 wherein saiddeposition chamber is an enclosed deposition chamber.
 17. The process ofclaim 12 wherein said anti-stiction coating is manufactured from aprecursor chosen from one of fluorinated octyltrichlorosilane (FOTS),fluorinated decyltrichlorosilane (FDTS), dichlorodimethylsilane (DDMS),octyltrichlorosilane (OTS) and octadecyltrichlorosilane (ODTS).
 18. Theprocess of claim 12 wherein said bump regions comprise a dielectricmaterial and wherein said anti-stiction coating comprises a materialthat coats only said dielectric material of said wafer.
 19. The processof claim 12, prior to said depositing an anti-stiction coating, furthercomprising depositing a carboxylic acid on said wafer.
 20. The processof claim 19 wherein said carboxylic acid is chosen from one of benzoicacid, perfluorobenzoic acid, lauric acid, and perfluorooctanoic acid.21. The process of claim 19 wherein said carboxylic acid deposits onlynon-bump regions of said wafer.
 22. A process of depositing ananti-stiction coating, comprising: enclosing a microelectromechanicaldevice (MEMS device) in a deposition chamber, said MEMS device includinga bump area; and depositing an anti-stiction coating only on said bumparea.
 23. The process of claim 22 wherein said coating comprises ahydrocarbon chain.
 24. The process of claim 22 wherein said bump area iscoated with SiO2 and wherein said anti-stiction coating coats said SiO2.25. The process of claim 22 wherein said MEMS device comprises aplurality of movable pixel plates, each of said pixel plates includingat least one bump area on a lower side thereof.
 26. The process of claim22 wherein said depositing comprises vapor deposition.
 27. The processof claim 22 wherein said depositing is conducted prior to packaging ofsaid MEMS device.
 28. The process of claim 22 wherein said MEMS deviceincludes an exposed surface, and wherein said exposed surface, excludingsaid bump area, comprises metallic material and wherein saidanti-stiction coating comprises a material that is non-reactive withmetallic material.
 29. The process of claim 22 wherein said depositingis conducted at a pressure of approximately 900 millitorr.
 30. Theprocess of claim 22 wherein said anti-stiction coating is manufacturedof a silane precursor, and wherein said silane is introduced to saiddeposition chamber at a partial pressure in a range of 100 to 300millitorr.
 31. The process of claim 22 wherein a catalyst is added tosaid deposition chamber during depositing of said anti-stiction coating.32. The process of claim 31 wherein said catalyst is chosen from one ofwater and acetic acid.
 33. The process of claim 31 wherein said catalystis added as a vapor in an amount at least equal to an amount ofvaporized anti-stiction precursor coating material.
 34. The process ofclaim 22 wherein said depositing comprises a chemical reaction, andwherein said reaction is completed in a time period of less than twentyminutes at an ambient temperature.
 35. The process of claim 22 furthercomprising, after said depositing, heating said MEMS device for a timeperiod of greater than forty minutes and less than one hundred minutesat a temperature in a range of 100 to 120 degrees Celsius.
 36. Theprocess of claim 35 further comprising, prior to said heating, flushingsaid deposition chamber with an inert gas.
 37. The process of claim 22wherein the deposited anti-stiction coating has a thickness of at mosttwenty Angstroms.
 38. The process of claim 22 wherein said MEMS deviceis pretreated prior to said depositing, said pretreatment comprisingplacing said MEMS device in an atmosphere chosen from one of a waterplasma and an oxygen plasma.
 39. The process of claim 22 wherein saidMEMS device is pretreated prior to said depositing, said pretreatmentcomprising placing said MEMS device in an atmosphere chosen from benzoicacid, perfluorobenzoic acid, lauric acid, and perfluorooctanoic acid.40. A microelectronic device, comprising: a substrate; a plate movablypositioned on said substrate, said movable plate including at least oneanti-stiction bump region; and a fluorinated hydrocarbon coatingpositioned only on said anti-stiction bump region of said device. 41.The device of claim 40 wherein said device comprises an opticalinterferometer.
 42. The device of claim 40 wherein said plate comprisesa reflective pixel plate.
 43. The device of claim 40 wherein saidmovable plate includes a surface facing toward said substrate andwherein said bump region is positioned on said surface.
 44. The deviceof claim 40 wherein said movable plate includes four corner regions anda central region, and wherein said movable plate includes a bump regionin each of said four corner regions and said central region.
 45. Thedevice of claim 40 wherein said bump region includes a dielectriccoating, and wherein said fluorinated hydrocarbon coating is positionedon said dielectric coating.
 46. The device of claim 40 wherein saidsubstrate and said movable plate are separated by a distance of at most500 nanometers.
 47. The device of claim 40 further comprising: aplurality of plates movably positioned on said substrate, each of saidmovable plates including at least one anti-stiction bump region; and afluorinated hydrocarbon coating positioned only on said anti-stictionbump regions of said device.
 48. The device of claim 40 wherein saidfluorinated hydrocarbon coating is manufactured from a precursor chosenfrom one of fluorinated octyltrichlorosilane (FOTS), fluorinateddecyltrichlorosilane (FDTS), perfluorobenzoic acid and perfluorooctanoicacid.
 49. A microelectronic device, comprising: a microelectronicsubstrate; a reflective plate movably positioned on said substrate; andan anti-stiction bump positioned on one of said substrate and saidplate, said bump including a hydrophobic coating positioned only on saidbump.
 50. The device of claim 49 wherein said hydrophobic coatingcomprises a fluorinated hydrocarbon.
 51. The device of claim 49 whereinsaid hydrophobic coating comprises a fluorinated long-chain silane. 52.The device of claim 49 wherein said substrate includes a plurality ofreflective plates positioned thereon, each reflective plate including atleast one anti-stiction bump having a hydrophobic coating positionedthereon.
 53. A microelectronic apparatus, comprising: means forsupporting; means for filtering movably mounted on said means forsupporting, means for spacing positioned between said means forsupporting and said means for filtering; and means for coatingpositioned only on said means for spacing.
 54. The apparatus of claim 53wherein said means for coating reduces capillary forces on a surface ofsaid means for spacing.
 55. The apparatus of claim 53 wherein said meansfor spacing is positioned on said means for filtering.
 56. The apparatusof claim 53 wherein said means for spacing is positioned on said meansfor supporting.
 57. The apparatus of claim 53 wherein said means forspacing includes a coating of dielectric material, and wherein saidmeans for coating is positioned on said coating of dielectric material.58. The apparatus of claim 53 wherein said means for spacing comprises abump extending outwardly a distance of at most 60 nanometers from one ofsaid means for supporting and said means for filtering.
 59. Theapparatus of claim 53 wherein said means for filtering includes acoating of carboxylic acid, said coating of carboxylic acid not coatingsaid means for spacing.
 60. A process of depositing an anti-stictioncoating, comprising: positioning a microelectronic device fordeposition, said microelectronic device including at least one bumpregion; and selectively reacting fluorodecyltrichlorosilane only on saidbump region of said microelectronic device.
 61. The process of claim 60wherein said positioning comprises positioning a wafer for saidreacting, said wafer including a plurality of microelectronic deviceseach including at least one bump region, and wherein said selectivelyreacting comprises selectively reacting said fluorodecyltrichlorosilaneonly on said bump region of said microelectronic devices.
 62. Theprocess of claim 60 further comprising, prior to said reacting,pretreating said bump region with one of a water plasma and an oxygenplasma.
 63. The process of claim 60 further comprising, prior to saidreacting, pretreating said bump region with a pretreatment material thatgenerates SiOH groups on a surface of said bump region.
 64. The processof claim 60 wherein said reacting takes place in a deposition chamber,said process further including adding a catalyst to said depositionchamber during said reacting, said catalyst chosen from one of water andacetic acid.
 65. The process of claim 60 wherein said positioning amicroelectronic device for deposition comprises placing said device in asealed package together with said fluorodecyltrichlorosilane.
 66. Thedevice of claim 1 wherein said movable plate includes a conductivesurface having a coating thereon of carboxylic acid.